Succeeded in making out the new material shows the effect of large changes in electrical resistance phenomenon and a magnetic field（磁場をかけると電気抵抗が大きく変化する現象の効果を示す新しい物質を作り 出すことに成功）

Professor Kikuchi of Fukui et al (condensed matter physics), but was able to give new substance to make a show the effect of "(CMR) colossal magnetoresistance" Symptoms vary greatly multiplied by the magnetic field is electrical resistance. Effect CMR, which is applied to parts information reading was incorporated into a storage device such as a hard disk (HD), that there is a possibility of finding new material this will lead to development of HD products, high-capacity cheaper .

CMR effect has been considered so far, with the nature are attracted to the magnet and manganese oxides occur in the metal of "ferromagnetic". German and French researchers have discovered the principle of the CMR effect the original received the Nobel Prize in Physics in 2007.

Professor Kikuchi is about four years ago, began a joint research with a group of Tsukuba, Ibaraki Prefecture Institute for Materials Science. Is the nature of the magnetic material is less strong, are attracted to the magnet material does not show the "antiferromagnetic" is for many, continued to study the issue using the CMR effect of antiferromagnetic material. As a result, was able to "sodium chromate" new material of ultrahigh-pressure heated over a million to more than a few atmospheres, such as chromium oxide, shows the effect of CMR.

To develop a product called HD more powerful, it is necessary to make the material a larger CMR effect, was to expand the scope of antiferromagnetic material was believed to Professor Kikuchi 's immune so far that, "he said leads to find or make a material or even greater.
I feel that it is focused on the substance of antiferromagnetism has led to success. I hope we tied in the manufacture of cheaper, high-capacity HD.



福井大の菊池教授（物性物理学）らが、磁場をかけると電気抵抗が大きく変化する現象「超巨大磁気抵抗（ＣＭＲ）」の効果を示す新しい物質を作り 出すことに成功した。ＣＭＲ効果は、ハードディスク（ＨＤ）などの記憶装置に組み込まれた情報読み取り部品に応用されており、今回の新物質発見が、より安価で大容量のＨＤ製品の開発などにつながる可能性があるという。

　ＣＭＲ効果はこれまで、マンガン酸化物など磁石に引き寄せられる性質を持つ「強磁性」の金属で起こると考えられてきた。ＣＭＲ効果の元の原理を発見したドイツとフランスの研究者は２００７年のノーベル物理学賞を受けた。
　菊池教授は約４年前、物質・材料研究機構（茨城県つくば市）のグループと共同研究を始めた。強磁性の物質は少なく、磁石に引き寄せられない性質である「反強磁性」を示す物質は多いため、反強磁性の物質を使ってＣＭＲ効果を出す研究を続けた。その結果、クロム酸化物などに数万気圧以上の超高圧をかけ て加熱し、ＣＭＲ効果を示す新しい物質「クロム酸ナトリウム」が出来た。
　より高性能なＨＤ製品を開発するには、ＣＭＲ効果がより大きな物質を作る必要があるといい、菊池教授は「これまで無縁だと思われていた反強磁性の物質にまで対象を広げたことで、より優れた物質を作ったり見つけたりすることにつながる」と話している。
　反強磁性の物質に着目したことが成功へつながった感じですね。より安価で大容量のHDの製造に結びついていくといいですね。